GTAW присадочные прутки для сплавов на основе никеля (NIBAS)
№ | Boehler | EN / ENISO | AWS | C | Si | Mn | Cr | Ni | Mo | Nb | Ti | Fe | Co | Ta | Al | |||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
1 | NIBAS 625-IG |
18274: | S Ni 6625 (NiCr22Mo9Nb) |
A5.14-05: | ERNiCrMo-3 | ≤ 0.02 | ≤ 0.2 | ≤ 0.3 | 22.0 | Bal. | 9.0 | 3.6 | + | ≤ 2.0 | ||||
2 | Thermanit Nicro 82 |
18274: | S Ni 6082 (NiCr20Mn3Nb) |
A5.14: | ERNiCr-3 | 0.02 | 0.1 | 3.0 | 20.0 | > 67 | 2.5 | ≤ 2.0 | ||||||
3 | NIBAS 70/20-IG |
18274: | S Ni 6082 (NiCr20Mn3Nb) |
A5.14-05: | ERNiCr-3 | 0.02 | ≤ 0.1 | 3.1 | 20.5 | Bal. | 2.6 | + | ≤ 1.0 | |||||
4 | NIBAS C 24-IG | 18274: | S Ni 6059 (NiCr23Mo16) |
A5.14-05: | ERNiCrMo-13 | ≤ 0.01 | 0.1 | <0.5 | 23.0 | Bal. | 15.8 | <1.0 | ||||||
5 | NIBAS 617-IG |
18274: | S Ni 6617 (NiCr22Co12Mo) |
A5.14-05: | ERNiCrCoMo-1 | 0.06 | 0.1 | 0.1 | 21.8 | Bal. | 9.0 | 0.3 | 0.5 | 11.0 | 1.3 | |||
6 | NIBAS C 276-IG | 18274: | S Ni 6276 (NiCr15Mo16Fe6W4) |
A5.14-05: | ERNiCrMo-4 | <0.012 | 0.1 | 16.0 | Bal. | 16.0 | 5.5 | T3.8 | V0.2 | |||||
7 | NIBAS 400-IG | 18274: | S Ni 4060 (NiCu30Mn3Ti) |
A5.14-05: | ERNiCu7 | 0.02 | 0.3 | 3.2 | Bal. | 2.4 | 1.0 | <1.0 | Cu29 |
Преимущества сварочных прутков Bohler для сплавов на основе никеля
Данный вид сварочных прутков используется:
- при сварке разнородных и трудносвариваемых металлов, работающих при температурных показателях до +300° С
- высоколегированных и жаростойких сталей
- в изготовлении трубопроводов
- в изготовлении трубопроводов
Сварка с использованием данного вида проволоки проводится в среде защитного газа – аргона.
За счет незначительного содержания углерода, проволока довольно устойчива к возникновению межкристаллической коррозии и к тому же имеет довольно широкий рабочий температурный диапазон от -196° до +550° С. Низкое содержание в нем диффузионно-подвижного водорода при высоких температурах почти полностью исключает возникновение трещин.